In order to improve the abrasion resistance of hydraulic structures, we investigated into the influence of volumetric content of PVA fiber on the strength and abrasion resistance of hydraulic concrete at different curing ages, and also analyzed the micro-morphology of PVA fiber-added concretes. Compared with baseline group, the concrete samples added with 0.2% PVA fiber in volumetric content boasts larger compressive strength, splitting tensile strength, and abrasion resistance strength, up by 20.8%, 33.2%, and 108.4%, respectively, yet meanwhile smaller wearing depth and mass wear rate, down by 34.2% and 3.9%, respectively. Micro-morphology analysis reveal that the PVA fiber is well dispersed in the concrete matrix and distributed in random directions when its volumetric content is 0.2%. In association with SEM analysis, we can conclude that PVA fiber of suitable dosage would enhance the strength and abrasion resistance of hydraulic concrete remarkably.
Key words
hydraulic concrete /
PVA fiber /
volumetric content /
abrasion resistance /
splitting tensile strength /
micro-morphology
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
References
[1] 吴 鹏. 钢纤维和PVA纤维对超高性能混凝土力学及抗冲磨性能影响研究[D]. 武汉:湖北工业大学,2019.
[2] HOLLAND T C, GUTSCHOW R A. Erosion Resistance with Sillica Fume Concrete[J]. Concrete International, 1987(3): 32-40.
[3] SONEBI M, BASSUONI M T. Investigating the Effect of Mixture Design Parameters on Pervious Concrete by Statistical Modelling[J]. Construction & Building Materials, 2013, 38(2): 147-154.
[4] 邵晓妹,范冬冬,马保国,等.CW弹性环氧砂浆抗冲磨性能及工程应用[J]. raybet体育在线
院报,2020,37(6):166-170.
[5] 田 竞,苏 骏,吴 鹏,等.纳米CaCO3对混凝土抗冲磨性能影响试验研究[J]. 混凝土与水泥制品,2020(6):9-12.
[6] 仲从春,李双喜,孟远远,等.超高性能混凝土抗冲磨性能试验研究[J]. 人民黄河,2021,43(1):16-20.
[7] FEBRILLET N, KIDO A, ITO Y, et al. Strength and Abrasion Resistance of Ultra High Strength Steel Fiber Reinforced Concrete[J]. Melanoma Research, 2000, 11(2): 63-71.
[8] 胡宏峡.黄河上游水电站抗冲磨混凝土试验研究[J]. 人民黄河,2020,42(10):142-147.
[9] 苏 骏,李 磊,吴 鹏,等.钢纤维与PVA纤维对超高性能混凝土强度及抗冲磨性能影响研究[J]. 混凝土与水泥制品,2019(11):39-42.
[10] 何 真,陈晓润,赵日煦,等.基于体积损失速率的混凝土抗冲磨性能评价[J]. 水力发电学报,2020,39(1):72-79.
[11] 涂天驰. 超高性能混凝土的抗冲磨性能研究[D]. 广州:华南理工大学,2018.
[12] 殷康蜓,孙海燕,龚爱民,等.PVA纤维对水泥基复合材料流动性能及力学性能的影响[J]. 粉煤灰综合利用,2018(4):19-22.
[13] 赵 杨,孙海燕,龚爱民,等.PVA纤维对水泥胶砂抗侵蚀性能的影响[J]. 混凝土与水泥制品,2021(3):62-65.
[14] 杜修力,田予东,窦国钦.纤维超高强混凝土的制备及力学性能试验研究[J]. 混凝土与水泥制品,2011(2):44-48,71.
[15] 邓中正,杨华全,肖开涛.掺纤维抗冲磨混凝土性能试验研究[J]. 混凝土,2017(4):8-10,14.
[16] 林小松,杨果林.钢纤维高强与超高强混凝土[M]. 北京:科学出版社,2002.
PDF(1501 KB)