地下水封洞库储存原油与环氧树脂灌浆材料相容性试验

李珍^1,2, 孙正^2,3, 邵晓妹^2,3

1.华南理工大学材料科学与工程学院,广州 510641;
2. 武汉长江科创科技发展有限公司,武汉 430010;
3.武汉理工大学材料科学与工程学院, 武汉 430070

收稿日期:2020-06-19 修回日期:2020-11-11 出版日期:2021-01-01 发布日期:2021-01-27
通讯作者: 孙正(1985- ),男,湖北广水人,工程师,硕士,主要从事水工修补材料研发与应用。E-mail: 284292995@qq.com
作者简介:李珍(1971-),女,湖南湘乡人,教授级高级工程师,博士研究生,主要从事水工新材料研发与应用。E-mail: lizhen@mail.crsri.cn
基金资助:
中央级公益性科研院所基本科研业务费项目(CKSF2017056/CL); 创新团队项目(CKSF2017060/CL)

Experiment on the Compatibility between Crude Oil in Underground Water-sealed Caverns and Epoxy Resin Grouting Material

LI Zhen^1,2, SUN Zheng^2,3, SHAO Xiao-mei^2,3

1. School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641,China;
2. Wuhan Changjiang Kechuang Science and Technology Development Limited Company,Yangtze River Scientific Research Institute, Wuhan 430010, China;
3. School of MaterialsScience and Engineering, Wuhan University of Technology, Wuhan 430070, China

Received:2020-06-19 Revised:2020-11-11 Online:2021-01-01 Published:2021-01-27

摘要/Abstract

摘要： 地下水封洞库储存原油与环氧树脂灌浆材料相容性表现为:2种材料长期接触后可能影响原油品质与灌浆材料固化物性能。为了明确2种材料长期接触的相容性,在模拟工况下开展原油静态浸泡试验,比较试验前后原油的元素含量与环氧固化物的质量、强度、分子结构、表面形貌等变化。结果表明:在40 ℃条件下,原油成分未发生显著变化,未对环氧树脂固化物的力学性能及结构形貌产生不利影响,二者间未发生化学反应。判断在正常运行条件下,原油与环氧树脂灌浆材料具有较好的相容性。

关键词: 地下水封洞库, 防渗, 原油, 环氧树脂灌浆材料, 相容性

Abstract: The compatibility between crude oil stored in underground water-sealed cavern and epoxy resin grouting material used for anti-seepage is defined as follows: the quality of crude oil and the mechanical properties of epoxy resin grouting material may change after long-term contact between the two organic materials. Static immersion test in crude oil was designed under simulated conditions to compare the changes of characteristic element content of crude oil and the quality, strength, molecular structure and surface morphology of epoxy resin cured materials before and after the immersion test. Results show that the composition of crude oil did not change significantly, nor did it adversely affect the mechanical properties and structural morphology of epoxy resin cured materials at 40 ℃. No chemical reaction occurred. It is concluded that the crude oil has good compatibility with epoxy resin grouting material under normal operating conditions.

Key words: underground water-sealed caverns, anti-seepage, crude oil, epoxy resin grouting material, compatibility

中图分类号:

TV441

李珍, 孙正, 邵晓妹. 地下水封洞库储存原油与环氧树脂灌浆材料相容性试验[J]. 院报, 2021, 38(1): 142-145.

LI Zhen, SUN Zheng, SHAO Xiao-mei. Experiment on the Compatibility between Crude Oil in Underground Water-sealed Caverns and Epoxy Resin Grouting Material[J]. Journal of Yangtze River Scientific Research Institute, 2021, 38(1): 142-145.

[1]	岑威钧, 赵昱豪, 李邓军, 刘力增. 深厚覆盖层上土工膜防渗堆石坝渗流场影响因素分析[J]. 院报, 2023, 40(4): 95-99,106.
[2]	郑星, 杨文超, 魏伟琼, 敖大华, 张胜, 徐永旺. 某特高土石坝防渗砾石土料P₅含量对其工程特性的影响试验研究[J]. 院报, 2023, 40(10): 103-107.
[3]	肖成志, 陶子琪, 张金利, 谢世平, 何顺辉, 吴东彪. GCL复合垂直防渗墙中污染物运移的一维解析解[J]. 院报, 2023, 40(1): 132-139.
[4]	陈华俊. 岩溶库区帷幕灌浆技术及其工艺参数优化[J]. 院报, 2022, 39(7): 144-148.
[5]	王艳丽, 刘晶, 王永明, 潘家军, 陈云. 复合土工膜与防渗墙连接的大型剪切试验研究[J]. 院报, 2021, 38(4): 75-80.
[6]	李珍, 冯菁, 韩炜, 邵晓妹. 水工建筑物混凝土新型防护材料研究与应用[J]. 院报, 2021, 38(10): 140-147.
[7]	周炳强, 黄灿新, 王团乐, 黄孝泉, 刘科, 许琦. 基于GEAS 3D的乌东德水电站防渗帷幕局部灌浆异常分析及处理[J]. 院报, 2020, 37(8): 155-160.
[8]	刘胜, 余波, 郑克勋, 马聪. 基于水文地球化学的坝基帷幕防渗性能分析[J]. 院报, 2019, 36(5): 121--127.
[9]	曹洋兵, 陈玉华, 黄真萍, 刘成禹, 邱冬冬. 地下水封洞库洞室轴线方向优化方法[J]. 院报, 2019, 36(5): 155-162.
[10]	吴庆华, 张伟, 邬爱清, 周华敏, 崔皓东. 堤防管涌险情研究进展[J]. 院报, 2019, 36(10): 39-44.
[11]	李少龙, 崔皓东. 渗透系数空间变异性对堤基渗透稳定影响的数值模拟[J]. 院报, 2019, 36(10): 49-52.
[12]	冯迪, 王媛, 高山, 余昌蔚. 分淮入沂整治工程典型堤段垂直防渗体防渗效果分析与评价[J]. 院报, 2019, 36(10): 180-184.
[13]	刘鹏,赵青,陈轶磊,金伍. 断层破碎带与洞室间距对地下水封洞库洞室稳定性的影响研究[J]. 院报, 2018, 35(8): 151-153.
[14]	邵晓妹,卢其波,李发权. 地下水封洞库水泥-水玻璃防渗灌浆材料耐久性试验研究[J]. 院报, 2018, 35(8): 154-158.
[15]	汪在芹. 高水头下不良地质体防渗补强技术研究与应用[J]. 院报, 2018, 35(5): 1-5.

地下水封洞库储存原油与环氧树脂灌浆材料相容性试验

Experiment on the Compatibility between Crude Oil in Underground Water-sealed Caverns and Epoxy Resin Grouting Material

PDF

可视化

摘要/Abstract