采用渣土对白云石进行煅烧改性,研究了煅烧渣土-白云石对水泥砂浆强度和膨胀性能的影响规律,并采用X射线衍射仪、扫描电子显微镜和能谱仪研究了掺煅烧渣土-白云石水泥的水化产物性能。结果表明:煅烧渣土-白云石可生成β-C2S和C12A7,且随着煅烧温度的提高,β-C2S和C12A7的含量增加;煅烧渣土-白云石能够有效促进复合水泥砂浆后期强度的发展,其中掺10%煅烧渣土-白云石水泥砂浆的90 d强度甚至高于纯水泥砂浆;此外,煅烧渣土-白云石中的MgO可水化生成Mg(OH)2,固相体积增加,促进了水泥砂浆的膨胀,且膨胀率随着煅烧渣土-白云石掺量的增加而增加。研究成果对于提高白云石在水泥混凝土中的应用及减轻建筑垃圾对环境的污染有一定参考价值。
Abstract
Dolomite was modified through calcination mixed with muck. The effects of calcined muck-dolomite on the strength and expansion properties of cement mortar were investigated. The hydration products of cement containing calcined muck-dolomite were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). Results show that β-C2S and C12A7 were generated in calcined muck-dolomite, and the content of β-C2S and C12A7 increased with the rising of calcination temperature. The incorporation of calcined muck-dolomite improves the strengths of blended cement mortar effectively at later age. Cement mortar containing 10% calcined muck-dolomite even gain a higher strength at 90 d than pure cement mortars. In addition, the hydration of MgO in calcined muck-dolomite gave rise to Mg(OH)2, resulting in the expansion of cement mortars, and the expansion rate augmented with the increase of dosage of calcined muck-dolomite. The research finding is of referential value for promoting the application of dolomite in cement concrete and for reducing the pollution of construction wastes.
关键词
渣土 /
白云石 /
煅烧 /
水泥砂浆强度 /
膨胀性能
Key words
muck /
dolomite /
calcination /
strength of cement mortar /
expansion properties
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] STUKOVNIK P, BOSILJKOV V B, MARINSEK M. Detailed Investigation of ACR in Concrete with Silica-free Dolomite Aggregate[J]. Construction and Building Materials, 2019, 216:325-336.
[2] KRISHNAN S, BISHNOI S. Understanding the Hydration of Dolomite in Cementitious Systems with Reactive Aluminosilicates Such as Calcined Clay[J]. Cement and Concrete Research, 2018, 108:116-128.
[3] 彭 园, 高育欣, 赵日煦, 等. 白云石粉用作混凝土掺合料的试验研究[J]. 混凝土与水泥制品, 2014(6):13-16.
[4] GARCIA E, ALFONSO P, LABRADOR M, et al. Dedolomitization in Different Alkaline Media: Application to Portland Cement Paste[J]. Cement and Concrete Research, 2003, 33 (9):1443-1448.
[5] DENG M, TANG M S. Mechanism of Dedolomitization and Expansion of Dolomitic Rocks[J]. 1993, 23(6):1397-1408.
[6] XU L L, DENG M. Dolomite Used as Raw Material to Produce MgO-based Expansive Agent[J]. Cement and Concrete Research, 2005, 35:1480-1485.
[7] MO L W, DENG M, TANG M S, et al. MgO Expansive Cement and Concrete in China: Past, Present and Future[J]. Cement and Concrete Research, 2014, 57:1-12.
[8] CAO F Z, MIAO M, YAN P Y. Effects of Reactivity of MgO Expansive Agent on Its Performance in Cement-based Materials and an Improvement of the Evaluating Method of MEA Reactivity[J]. Construction and Building Materials, 2018, 187:257-266.
[9] XIAO J Z, MA Z M, DING T. Reclamation Chain of Waste Concrete: A Case Study of Shanghai[J]. Waste Management, 2015, 48:334-343.
[10]YANG J, DU Q, BAO Y. Concrete with Recycled Concrete Aggregate and Crushed Clay Bricks[J]. Construction and Building Materials, 2011, 25(4):1935-1945.
[11]陈守开, 张政男, 郑永杰, 等. 再生骨料透水混凝土耐撞磨性试验研究[J]. raybet体育在线
院报, 2020, 37(7):153-159.
[12]陶 喆, 王瑞骏, 李 阳, 等. 受硫酸盐侵蚀的再生混凝土耐久性研究[J]. raybet体育在线
院报, 2019, 36(9):136-141.
[13]杨南如. 水热合成β-C2S的研究进展[J]. 建筑材料学报, 2011, 14(2):145-154.
[14]严 生, 蔡安兰, 周际东. C2S-C12A7-CaSO4· 2H2O-H2O系统水化机理[J]. 硅酸盐学报, 2004, 32(4):520-523.
[15]MO L W, DENG M, TANG M S. Effects of Calcination Condition on Expansion Property of MgO-type Expansive Agent Used in Cement-based Materials[J]. Cement and Concrete Research, 2010, 40:437-446.
基金
raybet体育在线
开放研究基金资助项目(CKWV2019757/KY);国家自然科学基金项目(51778003);广西建筑新能源与节能重点实验室开放课题项目(19-J-22-1);江苏省建设系统科技项目(2017ZD23)
PDF(1447 KB)