为充分发挥矿渣混凝土的绿色环保的优点,加快高掺量矿渣混凝土的应用,使用矿渣取代80%水泥制备了矿渣生态砂浆,利用硅粉作为基本性能调控材料,研究了硅粉掺量与矿渣砂浆力学和耐久性能的关系,并评价了矿渣砂浆的生态效率。研究结果表明,硅粉有助于缓解高掺量矿渣砂浆的缓凝问题,在10%硅粉掺量下,矿渣砂浆的凝结时间与基准组相近。另外,硅粉可显著改善矿渣砂浆的力学强度和耐久性,在最优掺量组 (5%)中,矿渣砂浆的28 d抗压强度和抗折强度均高于基准组。矿渣与(2.5%~10%)硅粉复掺时,砂浆的毛细吸水率降幅为8.83%~26.81%,电通量降幅为5.28%~36.87%。本研究通过使用矿渣和硅粉共同取代80%水泥,有效改善了矿渣砂浆的基本性能,提升了其生态效率,可为矿渣生态混凝土的应用与发展提供理论依据。
Abstract
To make full use of the prominent green feature of slag concrete and accelerate its practical application, we adopted silica fume as the strength adjustor to investigate its effect on the mechanical strength and durability of mortars with 80% slag. We also evaluated the ecological efficiency of slag mortars. Experimental results demonstrate that silica fume is such an effective material to mitigate the retarded setting of mortars with high amount of slag due to dilutive effect. When 10% silica fume was added, the setting time of slag mortar was close to that of the control group. Moreover, silica fume has exerted prominent effects on the mechanical strength and durability of mortars. With 5% silica fume added, both the 28-day compressive strength and the flexural strength of mortar were much higher than those of mortar without silica fume. Consequently, the durability of mortar was also greatly improved by incorporating slag and silica fume into mortars, i.e., the capillary water absorption and electric flux of mortar reduced 8.83%-26.81% and 5.28%-36.87%, respectively. In summary, through the combined use of slag and silica fume as the alternative to 80% cement to prepare mortars, we significantly ameliorated the performance of slag mortars as well as its ecological efficiency, hence providing theoretical basis for the application and development of concrete with high volume of slag.
关键词
矿渣砂浆 /
硅粉 /
力学强度 /
耐久性 /
生态效率
Key words
slag mortar /
silica fume /
mechanical strength /
durability /
ecological efficiency
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] RAFAT S, MOHAMMAD I K. Supplementary Cementing Materials[M].Heidelberg: Springer, 2011.
[2] 林宗寿. 矿渣基生态水泥[M]. 北京: 中国建材工业出版社, 2018.
[3] JOHARI M A M, BROOKS J J, KABIR S, et al. Influence of Supplementary Cementitious Materials on Engineering Properties of High Strength Concrete[J]. Construction and Building Materials, 2010, 25(5): 2639-2648.
[4] RASHAD A M, SADEK D M,et al. An Investigation on Portland Cement Replaced by High-volume GGBS Pastes Modified with Micro-sized Metakaolin Subjected to Elevated Temperatures[J]. International Journal of Sustainable Built Environment, 2017, 6(1): 91-101.
[5] SAJEDI F.Mechanical Activation of Cement-Slag Mortars[J]. Construction and Building Materials,2011,26(1):41-48.
[6] SIDDIQUE R,BENNACER R.Use of Iron and Steel Industry By-product (GGBS) in Cement Paste and Mortar[J]. Resources Conservation and Recycling,2012,69(12):29-34.
[7] FU X, HOU W, YANG C, et al. Studies on Portland Cement with Large Amount of Slag[J]. Cement and Concrete Research, 2000, 30(4): 645-649.
[8] ZHANG M, ISLAM J. Use of Nano-Silica to Reduce Setting Time and Increase Early Strength of Concretes with High Volumes of Fly Ash or Slag[J]. Construction and Building Materials, 2012, 34(5): 650-662.
[9] HOSAN A, SHAIKH F U A. Influence of Nano-CaCo3 Addition on the Compressive Strength and Microstructure of High Volume Slag and High Volume Slag-Fly Ash Blended Pastes[J]. Journal of Building Engineering, 2020, 27: 100929.
[10] El-CHABIB H, IBRAHIM A. The Performance of High-Strength Flowable Concrete Made with Binary, Ternary, or Quaternary Binder in Hot Climate[J]. Construction and Building Materials, 2013, 47(10): 245-253.
[11] SAJEDI F, RAZAK H A. Effects of Thermal and Mechanical Activation Methods on Compressive Strength of Ordinary Portland Cement-Slag Mortar[J]. Materials and Design, 2010, 32(2): 984-995.
[12] ASTM C191, Standard Test Method for Time of Setting of Hydraulic Cement by Vicat Needle[S]. Pennsylvania: ASTM International, 1999.
[13] ASTM C348, Standard Test Method for Flexural Strength of Hydraulic-Cement Mortars[S]. Pennsylvania: ASTM International, 2002.
[14] ASTM C1202, Standard Test Method for Electrical Indication of Concrete's Ability to Resist Chloride Ion Penetration[S]. Pennsylvania: ASTM International, 2012.
[15] ASTM C1585, Standard Test Method for Measurement of Rate of Absorption of Water by Hydraulic-Cement Concretes[S]. Pennsylvania: ASTM International, 2011.
[16] HAMIDI M, KACIMI L,CYR M, et al. Evaluation and Improvement of Pozzolanic Activity of Andesite for Its Use in Eco-efficient Cement[J]. Construction and Building Materials, 2013, 47(7): 1268-1277.
[17] ABDELKADER B,EI-HADJ K,KARIM E. Efficiency ofGranulated Blast Furnace Slag Replacement of Cement According to the Equivalent Binder Concept[J]. Cement and Concrete Composites, 2009, 32(3): 226-231.
[18] 蒋家奋. 矿渣微粉在水泥混凝土中应用的概述[J]. 混凝土与水泥制品, 2002, 29(3): 3-6.
[19] LI K, ZENG Q, LUO M, et al. Effect of Self-desiccation on the Pore Structure of Paste and Mortar Incorporating 70% GGBS[J]. Construction and Building Materials, 2014, 51(1): 329-337.
[20] RASHAD A M.An Investigation on Very High Volume Slag Pastes Subjected to Elevated Temperatures[J]. Construction and Building Materials,2015,74(1): 249-258.
[21] RICHARDSON I G.Tobermorite/Jennite-and Tobermorite/Calcium Hydroxide-based Models for the Structure of C-S-H: Applicability to Hardened Pastes of Tricalcium Silicate, Β-Dicalcium Silicate, Portland Cement, and Blends of Portland Cement with Blast-Furnace Slag, Metakaolin, or Silica Fume[J]. Cement and Concrete Research, 2004, 34(9): 1733-1777.
[22] DB 31/581—2012,矿渣粉单位产品能源消耗限额[J]. 北京:中国质检出版社, 2013, 32(1): 6-10.
[23] 段西京. 浅谈高纯度硅粉的深加工[J]. 铁合金,2015,46(9): 27-29.
基金
安徽省自然科学基金青年基金项目(1908085QE213);安徽高校自然科学研究重大项目(KJ2020ZD33);安徽省科技重大专项项目(202003a07020023)
PDF(3553 KB)